Biological composite material loaded with magnetic nanoparticles with core-shell structure, the preparation therefore and the application

ABSTRACT

A preparation method of  Bacillus subtilis  biological composite material loaded with Fe 3 O 4  magnetic nanoparticles with core-shell structure includes the following steps: 1) preparation of Fe 3 O 4  nanoparticles, 2) preparation of Fe 3 O 4 @mSiO 2  nanoparticles, 3) preparation of Fe 3 O 4 @mSiO 2 @MANHE nanoparticles; and 4) preparation of  Bacillus subtilis @Fe 3 O 4 @mSiO 2 @MANHE composite.

TECHNICAL FIELD

The present invention belongs to the technical field functional materials, the specific involves a load of magnetic nanoparticles with core-shell structure biological composite material, the preparation method of the composite material, and the use of the composite material to deal with the use of wastewater containing hexavalent chromium.

BACKGROUND TECHNOLOGY

Hexavalent chromium (abbreviated to Cr (VI)) as the swallowed poison/aspiration is extremely toxic, sensitization, birth defects, cancer and other serious consequences, and a lasting dangers to the environment. Unfortunately, chromium is widely used in numerous industrial processes, including leather tanning, pigment production, electroplating and ore refining. Because of extremely toxic and high solubility, hexavalent chromium goes into the living cells easily and produces reactive oxygen species (ROS), resulting in serious oxidative injuries to cell constituents. The main effects of hexavalent chromium for humans are dermatitis and aggressive reaction in lungs and nasal septum. So for treatment of wastewater containing hexavalent chromium needs to be received extensive attention of the society from all walks of life.

Due to have a combination of magnetic particles and the double advantage of nanoparticles, Fe₃O₄ magnetic nanoparticles have been widely applied in targeting drug carrier, cell separation, magnetic resonance, immunoassay, nucleic acid hybridization and biomedical fields. At the same time, the super paramagnetic material in the field of environmental protection monitoring also has the very good application prospect, can be used as adsorption material to deal with industrial waste water of heavy metal. However, magnetic Fe₃O₄ nanoparticles is difficult to be applied due to its easy oxidation, strong tendency of gathering, difficult to direct application.

In recent years, with clean and no secondary pollution and low cost advantage, such as biological method has gained extensive attention, but microbial processing pollutants also has its own disadvantages, processing cycle is long, the bacteria difficult separation from water and other factors restricted the practical application.

SUMMARY OF THE INVENTION

In view of the above, the invention combines the advantages of the adsorption method and the biodegradation method, and combines the two by modifying the Fe₃O₄ magnetic nanoparticles to the surface of Bacillus subtilis through the polymer shell covering the magnetic nanoparticle core, Cr(VI) can be rapidly enriched by the magnetic nanoparticles, and Cr (VI) can be rapidly degraded by microorganisms which are supported on the surface. The magnetic properties of the nanoparticles themselves can be separated rapidly from the water, which can overcome the bottleneck of its application and make it widely used in the treatment of heavy metal pollution.

First, the present invention provides a method for preparing a Bacillus subtilis biocomposite loaded with Fe₃O₄ magnetic nanoparticles having a core-shell structure, comprising the following steps:

(1) Preparation of Fe₃O₄ Nanoparticles

In this experiment, all the chemical agents were of analytical grade and were used without further purification. The spherical magnetic particles were prepared according to the literature with some modification. As usually, 2.02 g of Fe(NO₃)₃.9H₂O and 4.1 g of sodium acetate were dissolved in 50 mL of ethylene glycol (EG) with stirring for 30 min. The obtained solution was transferred to a Teflon-lined stainless-steel autoclave and heated at 180° C. for 6 h. Then the autoclave was naturally cooled to room temperature. The gained black magnetite particles were washed with ethanol for several times, and dried in vacuum at 60° C. for 5 h.

(2) Synthesis of Fe₃O₄@mSiO₂

The core-shell structured Fe₃O₄@mSiO₂ microspheres were prepared through a modified Stöber method. In a typical process, 0.10 g of obtained Fe₃O₄ particles were treated using 0.1 M HCl solution by ultrasonication for 20 min. Whereafter, the treated Fe₃O₄ particles were separated via centrifugation, washed with deionized water. At the same time, The Fe₃O₄ was dispersed in the mixture solution of 80 mL of ethanol, 20 mL of deionized water, and 1.0 mL of concentrated ammonia aqueous solution (28 wt. %). Afterward, 0.3 g of cetyltrimethylammonium bromide (CTAB) was added dropwise to the solution. After this, 0.25 mL TEOS was added dropwise into the solution under vigorous stirring for 6 h. After reaction for 6 h, the product was collected by magnetic separation and tautologically washed with ethanol and deionized water. The above coating process was redone twice. The structure-directing agent (CTAB) was removed with ethanol and deionized water for three times. The obtained precipitate was separated and washed with deionized water. Subsequently, the product was dried in vacuum at 60° C. for 24 h. The manufactured microspheres what was called Fe₃O₄@mSiO₂.

(3) Synthesis of Fe₃O₄@mSiO₂@MANHE

200 mg (Fe₃O₄@mSiO₂) of the nanoparticles obtained for 250 ml flask, the flask to add 150 ml acetonitrile, ultrasound 30 min, then add 3 ml KH550, mechanical agitation for the night.

The acid chloride derivative of ABCPA (Cl—ABCPA) was prepared by a reaction of ABCPA and PCl₅. ABCPA (3.0 g) was dissolved in dichloromethane (25 mL) and cooled to 0° C. PCL₅ (24 g) in 25 mL of CH₂Cl₂ was added into the above solution and stirred overnight. After the reaction, the excess PCl₅ was removed by filtration. The clear solution was added into 5-fold of hexane at 0° C., and 4,4-azo-bis(4-cyanopentanoicchloride) was obtained after filtration. Fe₃O₄mSiO₂-NH₂ nanoparticles (0.600 g) were added to 80 mL of dry dimethylformamide. After 0.5 h of ultrasonication, Fe₃O₄@mSiO₂—NH₂ (0.60 g) was dispersed in a mixture of 80 mL of CH₂Cl₂ and 2 mL of triethylamine, and Cl—ABCPA (2.5 g) in 25 mL of dry CH₂Cl₂ was added to the dispersion. After stirring at 0° C. for 2 h, the dispersion was stirred at room temperature overnight. Fe₃O₄@mSiO₂—ABCPA was obtained after filtration and washing with methanol and dichloromethane. Polymer on Fe₃O₄@mSiO₂—ABCPA sheets were prepared by free-radical polymerization. In a Schlenk flask, Fe₃O₄@mSiO₂—ABCPA (0.05 g), 4-vinylpyridine (4 mL) and N-Acryloxysuccinimide (0.7 g) monomer were dissolved in 9 mL of Cyclohexanone. After 0.5 h min sonication, the dispersion was stirred at 75° C. for 5 h. The resulting product was dissolved in acetone and centrifuged to remove the free polymer chains which were not anchored to the nanoparticles. The final product (FSM) was dried in vacuum at 50° C.

(4) Synthesis of Bacterial@Fe₃O₄@mSiO₂@MANHE

After strain B. subtilis ATCC-6633 was cultured for 48 h in 100 mL LB medium with shaking (120 rpm), the B. subtilis ATCC-6633 were harvested by centrifugation (5 min, 5500 g) and washed twice with PBS (sterile phosphate buffer solution). Then, the cell pellets were resuspended in PBS. Subsequently, 30 mg FSM was added into above system. Planktonic cells were cultivated at 30° C. with shaking (120 rpm) for 5 h. After that, BFSM were obtained by magnetic separation.

Preferably, in the above production process, the molar ratio between the ferrous sulfate heptahydrate and anhydrous sodium acetate in step (1) is 1:7.

Preferably, in the above-mentioned production method, the volume ratio of ethanol to water in the mixed solution of ethanol and water in step (2) is 4:1.

Preferably, in the above production method, the water used in the mixture of ethanol and water in step (2) is deionized water.

Preferably, in the above production method, the mass ratio between Fe₃O₄ nanoparticles, cetyltrimethylammonium bromide, and tetraethoxysilane in step (2) is 1:3:2.3.

Preferably, in the above preparation method, the ratio between the Fe₃O₄@mSiO₂ nanoparticles and the aminopropyltriethoxysilane in the step (3) is 200 mg:3 mL.

Preferably, in the above preparation method, the mass ratio between the amino-modified Fe₃O₄@mSiO₂ nanoparticles and 4,4′-azobis (4-cyanovaleryl chloride) in the step (3) is 1:20.

Preferably, in the above-mentioned production method, the mass ratio of the ABCPA-modified Fe₃O₄@mSiO₂ nanoparticles to the N-acryloyloxysuccinimide in step (3) is 1:20.

Preferably, in the above-mentioned production method, the ratio between the N-acryloyloxysuccinimide and the 4-vinylpyridine in step (3) is 1 g:10 mL.

Preferably, in the above production method, the inert gas in the step (3) is selected from any one of nitrogen, helium, and argon, preferably nitrogen.

Preferably, in the above preparation method, the mass ratio between the Bacillus subtilis (wet weight) and Fe₃O₄@mSiO₂@MANHE nanoparticles in step (4) is 100:1.

Preferably, in the above-mentioned production method, the PBS solution in step (4) has a pH of 7.

Secondly, the present invention provides a Bacillus subtilis biological composite material loaded with Fe₃O₄ magnetic nanoparticles having a core-shell structure prepared by the above-mentioned preparation method.

Finally, the present invention provides the use of a Bacillus subtilis biocomposite loaded with Fe₃O₄ magnetic nanoparticles having a core-shell structure as described above in the treatment of wastewater containing hexavalent chromium.

Compared with the prior art, the invention adopting the technical proposal has the following advantages:

(1) the raw materials used in the preparation process are inexpensive and easy to obtain;

(2) the operation is simple and convenient, the whole process does not use expensive equipment;

(3) The composite material of the invention has good adsorption degradation effect on Cr (VI) in water, and can be separated from water body quickly without causing secondary pollution and has wide application prospect.

APPENDED DRAWINGS

FIG. 1 shows the transmission electron microscopy (TEM) of Fe₃O₄ nanoparticles.

FIG. 2 shows the transmission electron microscopy (TEM) of Fe₃O₄@mSiO₂ nanoparticles.

FIG. 3 shows the transmission electron microscopy (TEM) of Fe₃O₄@mSiO₂@MANHE nanoparticles.

FIG. 4 is a scanning electron microscopy (SEM) image of Bacillus subtilis before and after treatment of Cr (VI).

FIG. 5 shows the transmission electron microscopy (TEM) of the B. subtilis@Fe ₃O₄@mSiO₂@MANHE composite.

FIG. 6 is the degradation curve of Cr (VI) and the OD600 curve of B. subtilis.

FIG. 7 shows the UV-Vis absorption spectra of Cr (VI) treated with B. subtilis at different times.

FIG. 8 shows the degradation of Cr (VI) by Bacillus subtilis, Fe₃O₄@mSiO₂@MANHE nanoparticles and Bacillus subtilis @Fe₃O₄@mSiO₂@MANHE composite.

DETAILED DESCRIPTION

The following will be combined with the appended drawings and the implementation of the specific case to make further explanation of the invention.Unless specifically noted that agents used in the following example, experimental material and equipment, etc. Can be obtained through commercial means.

EXAMPLE 1 Preparation of Fe₃O₄ Nanoparticles

In this experiment, all the chemical agents were of analytical grade and were used without further purification. The spherical magnetic particles were prepared according to the literature with some modification.⁴⁰ As usually, 2.02 g of Fe(NO₃)₃.9H₂O and 4.1 g of sodium acetate were dissolved in 50 mL of ethylene glycol (EG) with stirring for 30 min. The obtained solution was transferred to a Teflon-lined stainless-steel autoclave and heated at 180° C. for 6 h. Then the autoclave was naturally cooled to room temperature. The gained black magnetite particles were washed with ethanol for several times, and dried in vacuum at 60° C. for 5 h.

FIG. 1 shows the TEM of Fe₃O₄ nanoparticles. It can be seen, Fe₃O₄ nanoparticles dispersed and diameter of about 30 nm.

EXAMPLE 2 Preparation of Fe₃O₄@mSiO₂ Nanoparticles

The core-shell structured Fe₃O₄@mSiO₂ microspheres were prepared through a modified Stöber method. In a typical process, 0.10 g of obtained Fe₃O₄ particles were treated using 0.1 M HCl solution by ultrasonication for 20 min. Whereafter, the treated Fe₃O₄ particles were separated via centrifugation, washed with deionized water. At the same time, The Fe₃O₄ was dispersed in the mixture solution of 80 mL of ethanol, 20 mL of deionized water, and 1.0 mL of concentrated ammonia aqueous solution (28 wt. %). Afterward, 0.3 g of cetyltrimethylammonium bromide (CTAB) was added dropwise to the solution. After this, 0.25 mL TEOS was added dropwise into the solution under vigorous stirring for 6 h. After reaction for 6 h, the product was collected by magnetic separation and tautologically washed with ethanol and deionized water. The above coating process was redone twice. The structure-directing agent (CTAB) was removed with ethanol and deionized water for three times. The obtained precipitate was separated and washed with deionized water. Subsequently, the product was dried in vacuum at 60° C. for 24 h. The manufactured microspheres what was called Fe₃O₄@mSiO₂.

FIG. 2 shows the TEM of Fe₃O₄@mSiO₂ nanoparticles. It can be seen that Fe₃O₄ surface coated with mesoporous silica (mesoporous silicon dioxide, abbreviated as mSiO₂), and has good dispersion, the diameter of nanoparticles increased to 50 nm.

EXAMPLE 3 Preparation of Fe₃O₄@mSiO₂@MANHE Nanoparticles

200 mg (Fe₃O₄@mSiO₂) of the nanoparticles obtained for 250 ml flask, the flask to add 150 ml acetonitrile, ultrasound 30 min, then add 3 ml KH550, mechanical agitation for the night.

The acid chloride derivative of ABCPA (Cl—ABCPA) was prepared by a reaction of ABCPA and PCl₅. ABCPA (3.0 g) was dissolved in dichloromethane (25 mL) and cooled to 0° C. PCl₅ (24 g) in 25 mL of CH₂Cl₂ was added into the above solution and stirred overnight. After the reaction, the excess PCl₅ was removed by filtration. The clear solution was added into 5-fold of hexane at 0° C., and 4,4-azo-bis(4-cyanopentanoicchloride) was obtained after filtration. Fe₃O₄mSiO₂—NH₂ nanoparticles (0.600 g) were added to 80 mL of dry dimethylformamide. After 0.5 h of ultrasonication, Fe₃O₄@mSiO₂—NH₂ (0.60 g) was dispersed in a mixture of 80 mL of CH₂Cl₂ and 2 mL of triethylamine, and Cl—ABCPA (2.5 g) in 25 mL of dry CH₂Cl₂ was added to the dispersion. After stirring at 0° C. for 2 h, the dispersion was stirred at room temperature overnight. Fe₃O₄@mSiO₂—ABCPA was obtained after filtration and washing with methanol and dichloromethane. Polymer on Fe₃O₄@mSiO₂—ABCPA sheets were prepared by free-radical polymerization. In a Schlenk flask, Fe₃O₄@mSiO₂—ABCPA (0.05 g), 4-vinylpyridine (4 mL) and N-Acryloxysuccinimide (0.7 g) monomer were dissolved in 9 mL of Cyclohexanone. After 0.5 h min sonication, the dispersion was stirred at 75° C. for 5 h. The resulting product was dissolved in acetone and centrifuged to remove the free polymer chains which were not anchored to the nanoparticles. The final product (FSM) was dried in vacuum at 50° C.

FIG. 3 shows the TEM of Fe₃O₄@mSiO₂@MANHE nanoparticles. As can be seen from the figure, Fe₃O₄@mSiO₂ nanoparticles coated with a layer of polymer (MANHE), dispersion decreased, the diameter of nanoparticles to further increase to 100 nm.

EXAMPLE 4 Culture of Bacillus subtilis and Degradation of Cr (VI)

B. subtilis ATCC-6633 was obtained from Fujian Institute of Microbiology, China. Previous study suggested that the maximum hexavalent chromium resistance of B. subtilis ATCC-6633 is 40 mg/L. Planktonic cells were grown at 30° C. with shaking (120 rpm) for 48 h in modified LuriaeBertani (LB) liquid medium (pH=7) supplemented with 5 g/L NaCl, 10 g/L tryptone, 5 g/L yeast extract and 5 g/L glucose.

FIG. 4a shows the SEM of Bacillus subtilis Cr (VI), FIG. 4b shows the SEM of Bacillus subtilis after Cr (VI) degradation. From the figure, it can be seen that the surface of the cell before Cr (VI) was smooth and the surface of the cell after Cr (VI) was irregular.

EXAMPLE 5 Preparation of Bacillus subtilis@Fe₃O₄@mSiO₂@MANHE Composite

After strain B. subtilis ATCC-6633 was cultured for 48 h in 100 mL LB medium with shaking (120 rpm), the B. subtilis ATCC-6633 were harvested by centrifugation (5 min, 5500 g) and washed twice with PBS (sterile phosphate buffer solution). Then, the cell pellets were resuspended in PBS. Subsequently, 30 mg FSM was added into above system. Planktonic cells were cultivated at 30° C. with shaking (120 rpm) for 5 h. After that, BFSM were obtained by magnetic separation.

FIG. 5 shows the TEM of a B. subtilis@Fe₃O₄@mSiO₂@MANHE composite. It is clear from the figure that Fe₃O₄@mSiO₂@MANHE nanoparticles are modified to the surface of the cell.

EXAMPLE 6 Degradation of Cr (VI) (Concentration 40 ppm) by Bacillus subtilis and Test Results

The bacterial cells were collected by centrifugation and re-dispersed in waste water (100 mL) containing 40 ppm Cr (VI) and sampled at different times. The concentration of the solution at each time was measured by colorimetry and the UV- Spectrum.

FIG. 6 shows the degradation curve and OD600 curve of Cr (VI) treated by Bacillus subtilis. It can be seen that the concentration of Cr (VI) decreased and the OD600 of bacteria increased on the original basis, which indicated that Bacillus subtilis could tolerate Cr (VI) VI) can effectively survive in Cr (VI)—containing water. FIG. 7 shows the UV-Vis absorption spectra of Cr (VI) treated with Bacillus subtilis at different times. It can be seen that at 364 nm, the maximum absorption wavelength decreases with time, which indicates that the concentration of Cr (VI), And no absorption peak after 120 h. At 364 nm, the concentration of Cr (VI) in the surface solution has almost reached zero.

EXAMPLE 7 Effect Comparison of Treatment of Cr (VI) (Concentration 40 ppm) with Bacillus subtilis, Fe₃O₄@mSiO₂@MANHE Nanoparticles, Bacillus subtilis@Fe₃O₄@mSiO₂@MANHE Composite

Fe₃O₄@mSiO₂@MANHE nanoparticles and Bacillus subtilis@Fe₃O₄@mSiO₂@MANHE composites were weighed and dispersed in 40 ppm Cr (VI) solution. Samples were taken at different times and samples were taken and the corresponding UV-Vis absorption spectra were plotted.

FIG. 8 shows the degradation of Cr (VI) by Bacillus subtilis, Fe₃O₄@mSiO₂@MANHE nanoparticles and Bacillus subtilis@Fe₃O₄@mSiO₂@MANHE composite. It is clear from the comparison that Bacillus subtilis@Fe₃O₄@mSiO₂@MANHE composite has the highest removal rate of hexavalent chromium and the best effect.

In summary, the present invention realizes the degradation of Cr (VI) by adsorption on the side of Fe₃O₄@mSiO₂@MANHE nanoparticle to Bacillus subtilis, and has high degradation speed and high removal efficiency. More importantly, to achieve the magnetic separation of bacteria to solve the obstruction of microbial treatment of heavy metal pollution application problems. In addition, the production method disclosed in the present invention is easy to handle and the raw materials used are inexpensively available. Therefore, the magnetic nanometer biological composite material of the invention will have good application prospect in the future sewage treatment. 

1. A preparation method of a Bacillus subtilis biological composite material loaded with Fe₃O₄ magnetic nanoparticles with core-shell structure, which comprises the following steps: 1) preparation of Fe₃O₄ nanoparticles: add ferrous sulfate heptahydrate and anhydrous sodium acetate to ethylene glycol according to the mole ratio of ferrous sulfate heptahydrate:anhydrous sodium acetate=1:5 to 8, stir until the ethylene glycol solution is transparent and transfer the ethylene glycol solution to a high pressure reaction vessel and the ethylene glycol solution is sealed for 5 to 8 hours at 150 to 200 DEG C., after centrifugation, washing and drying, obtain the Fe₃O₄ nanoparticles; 2) preparation of Fe₃O₄@mSiO₂ nanoparticles: add the Fe₃O₄ nanoparticles obtained in step 1) to a mixture of ethanol and water, and disperse ultrasonically, under stirring, in accordance with the Fe₃O₄ nanoparticles:cetyltrimethylammonium bromide:tetraethoxysilane=1:3 to 5:2 to 3, add hexadecyltrimethylammonium bromide and tetraethoxysilane and keep at room temperature for 6 to 10 hours, after magnetic separation, washing and drying, obtain the Fe₃O₄@mSiO₂ nanoparticles; 3) preparation of Fe₃O₄@mSiO₂@MANHE nanoparticles: add the Fe₃O₄@mSiO₂ nanoparticles obtained in step 2) to N,N-dimethylformamide, disperse by ultrasonic, and keep stirring, under the conditions of Fe₃O₄@mSiO₂ nanoparticles:γ-aminopropyltriethoxysilane=50-100 mg:1 mL, add γ-aminopropyltriethoxysilane, stir overnight at room temperature, then centrifuge, wash and dry to obtain amino-modified Fe₃O₄@mSiO₂ nanoparticles; add the above-mentioned amino-modified Fe₃O₄@mSiO₂ nanoparticles into cyclohexanone and disperse by ultrasonic, under the conditions of inert gas protection and stirring, in accordance with the amino-modified Fe₃O₄@mSiO₂ nanoparticles:4,4′-azobis (4-4,4′-azobis (4-cyanovaleryl chloride)=1:20-30 in mass ratio, add 4,4′-azobis (4-4,4′-azobis (4-cyanovaleryl chloride) to the above system, stir overnight at room temperature, and subject to magnetic centrifugation, washing and drying to obtain ABCPA modified Fe₃O₄@mSiO₂ nanoparticles; add the ABCPA-modified Fe₃O₄@mSiO₂ nanoparticles to cyclohexanone and disperse by ultrasonic, under the conditions of inert gas protection and stirring, in accordance with the nano-particles of Fe₃O₄@mSiO₂ modified by ABCPA:N-acryloyloxysuccinimide=1:20 to 30 in mass ratio, and N-acryloyloxysuccinimide:4-vinylpyridine=1 g:10 to 15 mL, add N-acryloyloxysuccinimide and 4-vinylpyridine to the above system, reacting at 70-80 DEG C. for 0.5-1 hour, magnetic nanoparticles are obtained by magnetic centrifugation, washing and drying to obtain the Fe₃O₄@mSiO₂@MANHE nano-particles; 4) preparation of Bacillus subtilis@Fe₃O₄@mSiO₂@MANHE composite: add Bacillus subtilis to the PBS solution and dispers evenly, in accordance with the wet weight of Bacillus subtilis:Fe₃O₄@mSiO₂@MANHE nano-particles=50-100:1 in mass ratio, add the Fe₃O₄@mSiO₂@MANHE nano-particles obtained in step 3) to the above system, and placed on a constant temperature shaker at 30° C./120 rpm overnight, magnetic centrifuge, wash and dry to obtain the Bacillus subtilis biological composite material loaded with Fe₃O₄ magnetic nanoparticles with core-shell structure.
 2. The preparation method according to claim 1, characterized in that: the molar ratio between the ferrous sulfate heptahydrate and anhydrous sodium acetate described in step 1) is 1:7.
 3. The preparation method according to claim 1, which characterized in: the volume ratio of ethanol to water in the mixture of ethanol and water in step 2) is 4:1; the mass ratio of the Fe₃O₄ nanoparticles, cetyltrimethylammonium bromide, tetraethoxysilane described in the step 2) is 1:3:2.3.
 4. The preparation method according to claim 1, which characterized in: the ratio between the Fe₃O₄@mSiO₂ nanoparticles and the aminopropyltriethoxysilane described in the step 3) is 200 mg:3 mL; the mass ratio of the amino-modified Fe₃O₄@mSiO₂ nanoparticles to 4,4′-azobis (4-cyanovaleryl chloride) in step 3) is 1:20; the weight ratio between the ABCPA-modified Fe₃O₄@mSiO₂ nanoparticles and the N-acryloyloxysuccinimide described in step 3) is 1:20; the ratio between N-acryloyloxysuccinimide and 4-vinylpyridine in step 3) is 1 g:10 mL.
 5. The preparation method of claim 1, which characterized in: the inert gas in step 3) is selected from any of nitrogen, helium, and argon.
 6. The preparation method according to claim 5, which characterized in: the inert gas in step 3) is nitrogen.
 7. The preparation method according to claim 1, which characterized in: the mass ratio between the wet weight of Bacillus subtilis described in step 4) and the Fe₃O₄@mSiO₂@MANHE nanoparticles is 100:1.
 8. The preparation method according to claim 1, which characterized in: in step 4), the pH of said PBS solution is
 7. 9. A Bacillus subtilis biological composite material loaded with a Fe₃O₄ magnetic nanoparticle having a core-shell structure prepared by the preparation method according to claim
 1. 10. A method of treating waste water containing hexavalent chromium comprising applying the Bacillus subtilis biological composite material loaded with a Fe₃O₄ magnetic nanoparticle having a core-shell structure of claim 9 to the waste water. 